IGP-DURA®mix 334ME-A1
download PDF
Characteristics
- Deep matte
- Fine texture
- Pearl mica
Powder properties
Particle size:
< 100 μm
Solids:
> 99 %
Density:
1.3 kg/l-1.6 kg/l
Suitability for storage:
min. 24 months at ≤ 25 °C
in an unopened original container
Color tones:
RAL Metallic and individual metallic colors on request
Film properties
Tested on
Substrate:
Steel, 0.5mm
Film thickness:
60 μm - 80 μm
Object temperature:
170 °C, 15 min.
Mechanical tests
Cross-cut adhesion test
Gt 0
DIN EN ISO 2409 2020-12
Mandrel bending test
≤ 5 mm
DIN EN ISO 1519 2011
Impact test
≥ 10 inchp.
ASTM D 2794 1993
Erichsen cupping
≥ 3 mm
DIN EN ISO 1520 2007-11
Buchholz hardness
≥ 80
DIN EN ISO 2815 2003-10
Corrosion tests
Condensation water test, 1000h
No infiltration, no blisters
DIN EN ISO 6270-2 2018-04
Natural salt spray test, 1000h
No infiltration, no blisters
DIN EN ISO 9227 2017-07
Chemical tests
Organic solvents
Limited resistance to organic solvents.
Additional properties
Long term heat resistance
100°C
no yellowing until
Processing
Coating devices
All conventional electrostatic systems with corona charging.
For the construction and operation of powder coating plants, the following regulations must be complied with: ATEX RL 2014/34/EU, EN 50177, DIN EN 16985.
For the construction and operation of powder coating plants, the following regulations must be complied with: ATEX RL 2014/34/EU, EN 50177, DIN EN 16985.
Recommended film thickness
60 μm - 80 μm
A homogeneous coating result with textured coatings or article-and color specific differences in hiding power may require higher coating thicknesses. The corresponding processing guidelines must be observed.
For a pre-calculation of the required powder coating quantity, the necessary coating thickness must be determined for each article.
For a pre-calculation of the required powder coating quantity, the necessary coating thickness must be determined for each article.
Curing conditions
| TObject | t min | t max |
|---|---|---|
| 160 °C | 20 minutes | 40 minutes |
| 170 °C | 15 minutes | 30 minutes |
| 180 °C | 10 minutes | 20 minutes |
In order to determine ideal curing conditions, we recommend practical trials with the respective object and curing oven.
Reclaimability
Small portions of recovered powder can be added, automatically if possible, to the fresh powder. Important: Keep overspray to an absolute minimum. Processing instruction VR201.1 must be observed.
Further information
Packaging
20 kg cardboard box with inserted antistatic PE liner
500 kg cardboard container with 25 antistatic PE-liners each 20kg
Protection of coated parts
Coated parts should be packed after cooling with suitable materials without plasticizers. They should be stored protected from the weather to avoid the formation of condensation and thus water spots on the coating.
Cleaning
The coated parts must be cleaned according to the directives RAL-GZ 632 or SZFF 61.01. Technical Information IGP-TI 106 must also be observed when dealing with pearl mica effects.
Paint removal and disposal
After use, coated goods should be supplied to the normal recycling process. The disposal methods for sludges or residual powders must be observed in accordance with the local official provisions whilst taking Waste Code “080201 Coating Powder Wastes” in accordance with the European Waste Catalogue into consideration.
This application-related advice is given to the best of our knowledge. However, this information is non-obligatory and does not exempt you from carrying out your own tests. Application, use and processing of these products are beyond our control and are therefore on your responsibility. Consult the Safety Data Sheet prior to use.