IGP-DURA®one 6603A-G1 care
Matte low-temperature powder coating with smooth flow, ideal for indoor and outdoor applications. Finished with biocides.
download PDF
Proprietà
- Opaco
- Superficie liscia
- Tinte unite
- Industrial outdoor quality
- Contiene biocidi
Omologazioni
- Protetto da Sanitized®
Proprietà delle polveri
Granulometria:
< 100 μm
Corpi solidi:
> 99 %
Densità:
1.3 kg/l-1.6 kg/l
Stoccaggio:
min. 12 months a ≤ 25 °C
in an unopened original container
Color tones:
On request
Caratteristiche del film
Testato per
Substrati:
Aluminum (AlMg1), 0.8mm, chromated
Spessore:
60 μm - 80 μm
Temperatura dell’oggetto:
170 °C, 10 min.
Struttura superficiale
Brillantezza:
20-30 R’/60°
DIN EN ISO 2813 2015-02
Prove meccaniche
Cross-cut adhesion test
Gt 0
DIN EN ISO 2409 2020-12
Mandrel bending test
≤ 5 mm
DIN EN ISO 1519 2011
Impact test
≥ 20 inchp.
ASTM D 2794 1993
Erichsen cupping
≥ 5 mm
DIN EN ISO 1520 2007-11
Buchholz hardness
≥ 80
DIN EN ISO 2815 2003-10
Verifiche della resistenza a corrosione
Condensation water test, 1000h
No infiltration, no blisters
DIN EN ISO 6270-2 2018-04
Natural salt spray test, 1000h
No infiltration, no blisters
DIN EN ISO 9227 2017-07
Prove chimiche
Acids and alkalis
Good resistance to many dilute acids and alkalis.
Organic solvents
Limited resistance to organic solvents.
Contact to sulfur containing compounds could lead to deactivation of the silver based additive.
The usage in industrial atmosphere should be therefore avoided.
The usage in industrial atmosphere should be therefore avoided.
Applicazione
Pretrattamento
The substrate must be free from oil, grease and oxidation products. The pretreatment depends on the type of substrate and the corrosion protection to be achieved. We recommend the following pretreatments:
Alluminio
- Chromating according to DIN EN 12487
- Pre-anodization
- Chrome-free pretreatment according to GSB International and QUALICOAT specifications
Acciaio
- Zinc phosphating
Acciaio zincato
- Zinc phosphating
- Chrome (III) passivation
- Chromating according to DIN EN 12487
For improved corrosion protection for applications on steel / galvanised steel, the use of corrosion protection primer IGP-KORROPRIMER 18 is recommended.
The suitability of the pretreatment method used is generally to be tested by the coater in advance with appropriate test methods. The minimum requirement for aluminium substrates / galvanised steel components is to carry out a boiling water test with a subsequent cross-cut adhesion and tape test. We refer to the guidelines of the GSB International, Qualicoat and Qualisteelcoat certifications. For further information: see also our special leaflet on pre-treatment (IGP-TI 100).
Impianti di verniciatura
All conventional electrostatic systems with corona charging.
For the construction and operation of powder coating plants, the following regulations must be complied with: ATEX RL 2014/34/EU, EN 50177, DIN EN 16985.
For the construction and operation of powder coating plants, the following regulations must be complied with: ATEX RL 2014/34/EU, EN 50177, DIN EN 16985.
Spessore del film consigliato
60 μm - 80 μm
A homogeneous coating result with textured coatings or article-and color specific differences in hiding power may require higher coating thicknesses. The corresponding processing guidelines must be observed.
For a pre-calculation of the required powder coating quantity, the necessary coating thickness must be determined for each article.
For a pre-calculation of the required powder coating quantity, the necessary coating thickness must be determined for each article.
Condizioni di cottura
| Toggetto | t min | t max |
|---|---|---|
| 160 °C | 15 minutes | 25 minutes |
| 170 °C | 10 minutes | 20 minutes |
| 180 °C | 8 minutes | 15 minutes |
Per accertare le condizioni di cottura migliori si consiglia, in ogni caso, di effettuare prove pratiche con il rispettivo oggetto e forno di polimerizzazione.
Application
A voltage setting of minimum 50kV is recommended for spraying.
Ideally using a discharge ring (“super corona”) otherwise set the current limit to ≥5µA.
Non-consideration may lead to a significant higher gloss level.
Ideally using a discharge ring (“super corona”) otherwise set the current limit to ≥5µA.
Non-consideration may lead to a significant higher gloss level.
Recupero
Small portions of recycled powder can be added, automatically if possible, to the fresh powder. Important: Keep overspray to an absolute minimum.
Altre informazioni
Imballaggio
20 kg cardboard box with inserted antistatic PE liner
500 kg cardboard container with 25 antistatic PE-liners each 20kg
Protezione delle superfici verniciate
Coated parts should be packed after cooling with suitable materials without plasticizers. They should be stored protected from the weather to avoid the formation of condensation and thus water spots on the coating.
Pulizia
The coated parts must be cleaned according to the directives RAL-GZ 632 or SZFF 61.01.
Rimozione e smaltimento della pittura
After use, coated goods should be supplied to the normal recycling process. The disposal methods for sludges or residual powders must be observed in accordance with the local official provisions whilst taking Waste Code “080201 Coating Powder Wastes” in accordance with the European Waste Catalogue into consideration.
Le presenti informazioni di natura tecnica relative all’utilizzo sono fornite sulla base delle conoscenze attuali. Tuttavia devono essere considerate come indicazioni non vincolanti che non esonerano dall’effettuazione di controlli autonomi. Utilizzo, destinazione e applicazione di prodotti hanno luogo senza possibilità di controllo da parte nostra e, pertanto, soggiacciono esclusivamente alla vostra responsabilità.